基于电阻法的高浓磨浆机磨片磨损测量实验研究

打开文本图片集

中图分类号：TS733+.3 文献标识码：A DOI：10.11980/j.issn.0254-508X.2025.04.015

作者简介：，在读硕士研究生；主要从事微小磨损间接测量等方面的研究。

Experimental Studyon Wear Measurement of High ConsistencyRefiner Plate Based on Resistance Method

CHENHuiqin'ZHANG Zhiyi²*LIShishen1 （1.CollegeofMechanical Engineering，Beihua University，Jilin，JilinProvince，; 2.Engineering TrainingCenterofBeihua University，Jilin，JilinProvince，） （*E-mail： zyzhang6@163.com）

Abstract：Amethodwasproposedforolinemeasurementofgridingplatewearusingawearod.IndirectdetectionofmicrowearofdiferentwearrodmaterialssuchsQ2arbstel，Calstel，HSspedsteel，andgroealloysteet using the resistance method，and the relationship between voltage（ U ）and wear amount（ X ）under different materials and shapes of high chrome alloy steel was explored. The effect of current on the U-X curve was also investigated，and a quadratic regresson model was established to describe the relationship between U and X . The results showed that under a given current， the U X curves of the four materials and diferentshapesofoealystleidaoveallicreasingtredAstheaireass，geofsquareadclidical high chrome alloy steel increased uniformly and significantly.The current basicallydid not affct the U-X curvevariation trend of square and cylindricalighoeallstee.TeperfoaceiicatorsSEadMAEfopredictingtearofclidricalgholel were 0.005 68 and 0.004 66，respectively.

Key words：high consistency refiner；wear rod；wear measurement；characteristic curve；fitted model

造纸工业是国民经济的关键基础产业，其发展水平体现国家或地区的科技与经济实力。（剩余9049字）